• BASF Patents Electrocoat

    February 7, 2013
    U.S. 8,192,603 B2 BASF Coatings GmbH has been granted a patent for an aqueous coating composition comprised of a metal oxide selected from the group consisting of bismuth oxide, vanadium oxide, manganese oxide, cobalt oxide, zinc oxide, strontium oxi…

  • DuPont Patents High Solids Coatings

    February 7, 2013
    U.S. 8,197,905 B2 E I du Pont de Nemours and Co. has been granted a patent for a process which is comprised of applying a solvent-based coating having a low content of VOCs of 2.1 lbs/gal and below on a substrate to obtain a clear coating layer of a…

  • Dainichiseika Color and Chemicals Patents Pigment Dispersants

    January 15, 2013
    U.S. 8,163,839 B2 Dainichiseika Color and Chemicals Mfg. Co. has received a patent for a process for the production of a pigment dispersant comprised of polymerizing (a′) 5% to 30% weight of at least one of an aromatic vinyl monomer and a heter…

  • DSM Patents Hydrophobic Coating

    January 15, 2013
    U.S. 8,187,707 B2 DSM IP Assets B.V. has been awarded a patent for a coated substrate comprised of a substrate and a superhydrophobic film or coating on the substrate, wherein the superhydrophobic film or coating has a static water contact angle abov…

  • Finished Unlimited Patents Radiation Cured Coatings

    January 15, 2013
    U.S. 8,304,032  Finished Unlimited has obtained a patent for a curable coating composition suitable for use on composite substrates such as plastic composites, cementitious composites, ceramic composites, and engineered wood, or on plastic mater…

  • PPG Patents Electrodepositable Coatings

    January 15, 2013
    U.S. 8,168,700 B2 PPG Industries has been granted a patent for an electrodepositable coating composition comprised of a resinous phase dispersed in an aqueous medium. The resinous phase is comprised of (a) an active hydrogen-containing, cationic salt…

  • UCL Business Patents Thermochroic Coatings

    January 15, 2013
    U.S. 8,197,721 B2 UCL Business PLC has been awarded a patent for a method of producing thermochromic vanadium oxide by atmospheric pressure chemical vapor deposition (APCVD) comprised of the steps of mixing together a vanadium precursor, an oxygen pr…

  • Paint for Low-Emissive Paint

    January 15, 2013
    U.S. 8,187,503 B2 Totalforsvarets Forskningsinstitut has been granted a patent for a method for reducing thermal emissions from a surface in the infrared wavelength range of 2.5-25 μm, which is comprised of applying a paint to the surface, the pai…

  • Valspar Patents Low-Temp Cure Coating

    December 20, 2012
    U.S. 8,198,348 B2 Valspar Sourcing has been granted a pat- ent for a method of making a coating composition comprised of reacting the following components to form a coating composition: a first component A, com- prised of: approximately 20% weight to…

  • Evonik Patents Aluminum Oxide Powder, Dispersion and Coating

    December 20, 2012
    U.S. 8,197,791 B2 Evonik Degussa GmbH has obtained a patent for an aluminium oxide powder in the form of aggregates of primary par- ticles, wherein each particle has a BET surface area of from 10 to 90 m2/g and is comprised of as crystalline phases,…

  • Henkel Patents Adhesive

    December 20, 2012
    U.S. 8,197,944 B2 Henkel has been awarded a patent for a one-component structural adhesive that has a flow limit of at least 1500 Pa, a flow rate of <50 grams/minute, and an initial adhesion of more than 30 g/cm2, and that is comprised of 10% to 7…

  • PPG Patents Low Temp, Moisture Curable Coating

    December 20, 2012
    U.S. 8,168,738 B2 PPG Industries has been granted a patent for a coating comprised of a binder com- prised of a saturated polymer comprised of silyl functional groups and having a silyl equivalent weight of at least 150; an ungelled, secondary amine-…

  • Sachtleben Pigments Patents Titanium Dioxide

    December 20, 2012
    U.S. 8,182,602 B2 Sachtleben Pigments has been granted a patent for a method of preparing a well- dispersable, rutile-structured, microcrys- talline titanium dioxide product having a crystal size of less than 60 nm from a TiO2 starting material, the…

  • Imperial Chemical Industries Patents Low VOC Coating

    December 20, 2012
    U.S. 8,197,902 B2 Imperial Chemical Industries has ob- tained a patent for a pigmented, aqueous coating comprised of an aqueous disper- sion of non-crosslinkable addition oligo- mer of weight average molecular weight of 5000 to 15000 Daltons and calc…

  • United Technologies Patents Durable Coating

    December 20, 2012
    U.S. 8,187,989 B2 United Technologies has been granted a patent for a coating comprised of 30% to 80% weight of a hard carbide material and 20% to 70% weight of a lubricating material incorporated with the hard car- bide material, wherein the thermal…