• Login
    • Join
  • FOLLOW:
  • Subscribe Free
    • Magazine
    • eNewsletter
    Checkout
    • Magazine
    • News
    • Research
    • Markets & Technologies
    • Raw Materials
    • Top Companies
    • Directories
    • Jobs
    • Events
    • Microsites
    • More
  • Magazine
  • News
  • Research
  • Markets & Technologies
  • Raw Materials
  • Top Companies
  • Directories
  • Jobs
  • Events
  • Microsites
  • Current / Back Issues
    Features
    Business Corner
    Editorial
    Digital Edition
    eNewsletter Archive
    Our Team
    Editorial Guidelines
    Subscribe Now
    Advertise Now
    World Reports
    eBook
    Top Features
    Mixing Equipment Directory

    The Wood Coatings Market

    Antimicrobial Coatings Market

    Additives Update

    Pigment Supplier Directory
    Breaking News
    Online Exclusives
    Distributor News
    Financial News
    Paint & Coatings Manufacturer News
    People In the News
    Price Increases
    Product News
    Video Bites
    Raw Materials & Equipment
    Suppliers News
    Live From Shows
    Top News
    Nippon Paint Marine Wins Korea Export Award

    Universal Display Corporation, PPG Expand Global Production of UniversalPHOLED Materials

    PPG Introduces Premium Iso-free Primer Surfacer, Catalyst

    ECOS Paints Launches Lisa Tharp Colors

    OQ Chemicals Increases Carboxylic Acids, Esters Prices
    Top Companies report
    Market Research
    White Papers / Tech Papers
    Technical Papers
    Product Spec Sheets
    World Reports
    Adhesives and Sealants
    Aerospace Coatings
    Architectural Coatings
    Automotive Coatings
    Automotive Refinish
    Business Operation
    Color Trends & Forecast
    Construction Chemicals
    Corrosion Control
    Industrial Coatings
    Laboratory Equipment
    Marine Coatings
    Market Trends & Forecast
    Powder Coatings
    Production Equipment
    Radcure Coatings
    Special Purpose Coatings
    Wood Coatings
    "Green" Coatings

    Nippon Paint Marine Wins Korea Export Award

    ECOS Paints Launches Lisa Tharp Colors

    BYK-Gardner Launches VMA-Getzmann TORUSMILL

    Sensory Analytics Announces Issuance of Broad New Patent Covering Coating Thickness Measurement

    Union Process Develops Attritor for Inks, Coatings Supplier
    Additives
    Binders
    Pigments
    Solvents

    OQ Chemicals Increases Carboxylic Acids, Esters Prices

    Arkema Reports Full-year 2020 Results

    New Increase in Kynar Fluoropolymer Capacities at Arkema's Chinese Site

    Emerald Kalama Chemical Acquired by LANXESS

    Raw Material Suppliers, Distributors Part of Recent M&A Activity
    Buyers Guide
    Company Capabilities
    Distributor Guide
    Add New Company
    International Buyers Guide Companies
    Clariant Additives

    Active Minerals

    Keim Additec Surface USA LLC

    Eagle Specialty Products

    Siltech Corporation
    Industry Events
    Webinars
    Live From Show Event
    Top Events
    Surface Finishing Mexico 2021

    Cleveland Coatings Society Zoom Meeting

    Cleveland Coatings Society Zoom Meeting

    PCI Powder Coating Week

    Southern Society for Coatings Technology Annual Meeting and Technical Conference
    Companies
    White Papers/Tech Papers
    Product Spec Sheets
    Equipment
    Literature/Brochures
    Videos
    International Buyers Guide Companies
    Shepherd Color Company, The

    Pilot Chemical Company

    Siltech Corporation

    Eagle Specialty Products

    Clariant Additives
    • Magazine
      • Current / Back Issues
      • Features
      • Editorial
      • Business Corner
      • Digital Edition
      • eNewsletter Archive
      • Editorial Guidelines
      • Subscribe Now
      • Advertise Now
    • Breaking News
    • Directories
      • Buyers Guide
      • Distributor Guide
      • Corporate Capabilities
      • Trade Associations
      • Add Your Company
    • Markets & Technologies
      • Adhesives and Sealants
      • Aerospace Coatings
      • Architectural Coatings
      • Automotive Coatings
      • Automotive Refinish
      • Business Operation
      • Color Trends & Forecast
      • Construction Chemicals
      • Corrosion Control
      • Industrial Coatings
      • Laboratory Equipment
      • Marine Coatings
      • Market Trends & Forecast
      • Powder Coatings
      • Production Equipment
      • Radcure Coatings
      • Special Purpose Coatings
      • Wood Coatings
      • "Green" Coatings
    • Raw Materials
      • Additives
      • Binders
      • Pigments
      • Solvents
    • World Reports
      • Africa Report
      • China Report
      • India/Asia Pacific Report
      • Europe Report
      • Latin America Report
      • Market Research
      • Russian Report
    • Top Companies
    • Online Exclusives
    • Slideshows
    • Experts Opinions
    • Blog
    • eBook
    • Infographics
    • Videos
    • Podcasts
    • Whitepapers
    • Jobs
    • Microsites
      • Companies
      • White Papers/Tech Papers
      • Product Spec Sheets
      • Equipment
      • Literature/Brochures
      • Videos
    • Events
      • Industry Events
      • Live From Show Event
      • Webinars
    • About Us
      • About Us
      • Contact Us
      • Advertise With Us
      • Privacy Policy
      • Terms of Use
    Features

    Overcoming Adhesion Failures of UV Coatings with Atmospheric Plasma Treatment

    ...

    Overcoming Adhesion Failures of UV Coatings with Atmospheric Plasma Treatment
    Overcoming Adhesion Failures of UV Coatings with Atmospheric Plasma Treatment
    Related CONTENT
    • PPG Introduces Premium Iso-free Primer Surfacer, Catalyst
    • Raw Material Suppliers, Distributors Part of Recent M&A Activity
    • IFS Coatings Launches IFS Pureflex FBE for Rebar
    • AkzoNobel Opens R&D Lab Dedicated to Low Cure Powder Coatings
    • AkzoNobel Offers 100% UV Cured Wood Coatings
    Paul Mills and Andrew Stecher, Plasmatreat USA, Elgin, IL10.19.15
    Abstract

    UV curable coatings are becoming an increasingly popular alternative to conventional coatings.  Compared with thermal coatings, UV coatings provide a number of benefits to plastic part manufacturers including enhanced appearance, improved performance, and various process worker safety, and environmental advantages. But, same high speed curing and highly-crosslinked chemistry that underlie these benefits can also make adhesion failures more likely.  This paper examines the problem of adhesion common to UV curable liquid and powder coatings, and describes some tradeoffs associated with popular methods to reduce adhesion problems. Atmospheric plasma provides an especially attractive method of enhancing adhesion of UV cure coatings to a wide range of plastic materials.

    Background

    Since the early 1970s, UV curable coatings have gained slow, but steady acceptance as an alternative finishing technique for a wide range of substrates from wood flooring, to glass optical components, and from pipe and tube to plastic cosmetics containers. Today for example, nearly all polycarbonate headlight lenses, most plastic commercial eyewear, and a large percentage of plastic consumer electronic devices are UV coated. 

    A number of factors are believed to be responsible for the success of UV coatings growth (Cohen, 2012).  First, UV curing is an extremely rapid process compared with conventional thermal baking and curing. UV formulations cure almost instantaneously when exposed to ultraviolet light (Walton, 2012). By contrast, conventional waterborne and solvent borne systems require substantial oven dwell times and relatively higher temperatures. This makes UV curing attractive for coating applications such as graphic arts and printing, optical fiber coating, wood molding and panel finishing, and similar high speed applications.

    This speed advantage is even more impressive when comparing traditional thermoset powder coatings to UV curable powders.  Once applied, traditional thermoset powder coatings require a substantial amount of time in order for the powder to melt and flow to produce a smooth, continuous film. This melt/flow process is important to achieve both aesthetic and performance qualities.  After flowing, thermoset powder coatings also require substantial dwell time at high temperatures to achieve the complete polymer cross-linking needed for full performance. Taken together, this two-stage process routinely requires between 20 and 60 minutes (Walton, 2012).  By contrast, UV curable powder coatings also use thermal energy to melt and flow the powder coating, but rely on ultraviolet light instead of heat to achieve crosslinking. With UV cure powders, total process times of less than 10 minutes have been reported (Schwarb and Knoblauch, 2011) .

    Another feature of UV coatings is their tough surface properties; particularly high scratch and mar resistance. It is these properties that make UV coatings especially well-suited for applications such as hardwood flooring, optical coatings, and CD/DVD coatings where surfaces often must take a good deal of abuse. The surface durability of UV coatings stems from the high cross-link density common to UV formulations particularly those using popular (meth)acrylate chemistry (Schwalm, 2006).  But while high crosslink density provides tough surfaces, it has some drawbacks as well. For example, physical shrinkage is closely associated with the high crosslink density found in UV films. The acrylate monomers and oligomers shrink considerably as longer-distance Van der Waals forces are replaced by strong but shorter covalent bonds. Schwalm (2006) suggest that shrinkage as high as 35% can occur in UV formulations. Shrinkage causes internal stress that can result in defects and dimensional changes leading to decreased adhesion (Jian et al. 2013).

    A third feature of UV cure liquid coatings is that instead of conventional organic solvents, UV formulas frequently employ low molecular weight additives such as monomers and other reactive diluents.  These are fully consumed in the curing process, leading to the notion that some UV coatings are “100% solids” materials.  This feature has attracted the attention of government regulatory agencies and environmentally conscious manufacturers (Loof, 2001). But again, while eliminating solvents results in fewer hazardous air pollutants and lower VOCs, removing these solvents presents a challenge to attaining adhesions, since solvents help wet-out the surface of the part. Powder coatings emit virtually no VOCs or hazardous air pollutants, and contain no solvents (Whitfield, 1995). However, most powder applicators must invest heavily in chemical pretreatment prior to powder coating to attain sufficient adhesion.

    To make matters worse, many popular plastics are tough to begin with.  Their surfaces are more chemically inert. Table 1 illustrates this by comparing the surface energy of common plastics with the surface energy required to attain adequate adhesion for various coating technologies.  UV curable coatings require higher surface energy to achieve adequate performance than their conventional counterparts.

    Taken together, UV coatings provide attractive benefits but also present formidable obstacles to achieving adhesion for coatings, inks and adhesives.  The inherent high cross-link density of UV formulas results in mechanical stresses that, combined with the absence of conventional solvents, and their higher surface energy requirements, make it more difficult to ensure proper adhesion. 

    Improving Adhesion to Plastic

    A number of possible routes for improving the adhesion of coatings to plastic substrates are available. The most popular alternatives include reformulating the coating, adding adhesion promoting agents to the process, modifying the composition of the substrate, applying an additional layer of primer coating, or raising the surface energy level of the substrate using corona, flame or plasma surface treatment (Ryntz, 1994).

    Frequently the presence of contaminants is also a factor in adhesion failures. Contaminants include soils, mold release agents, or oily fingerprints or can stem from chemicals within the plastic as materials migrate to the surface. Wiping parts manually with solvent creates a concern for worker safety since exposure to caustic cleaners and harmful solvents, as well as hazardous VOCs. Manual wiping is also time consuming, so automated methods like plasma removal are better suited to high speed processing, and thin deposits of contamination.

    Reformulating a coating is another potential path, but it is often means sacrificing other coating properties (Burak, 2003). Suppliers are often unwilling to modify coatings unless the user is willing to pay for additional formulation and tolerate long delays as new versions of the coating are tested. Also, improvements in adhesion can sometimes come only at the expense of other properties such as changes in gloss, less surface hardness, or an increase in the coating’s cost. In some industries, reformulation may also require requalification or recertification of the material or process, incurring additional testing time and cost.

    Another alternative is to modify the composition of the substrate itself. But since designers often choose plastics for a range of other mechanical properties such as machinability, weight, mold time or dimensional stability, replacing a plastic may be difficult if there are few substitutes that provide these desired properties, or can meet the target cost (Ryntz, 1998).

    Still another route to attaining adhesion is to incorporate a thin ‘tie-coat’ of chlorinated polyolefin to assist in promoting adhesion of the coating to polyolefins. The thickness of the tie coat critical to obtaining good adhesion. If the coat is too thick, cohesive failure within the tie-coat can occur, while too thin a tie coat will not provide adhesion (Ryntz, 1994).
    The remainder of this article discusses attaining adhesion by treating the substrate surface in order to remove contaminants and to increase the surface energy so enable strong adhesion. This method is safe, economical, does not require reformulation of either the coating or the substrate, or applying an additional coating.

    Adequate adhesion requires the presence of strong forces where the coating and surface meet.  Plasma can significantly increase the surface energy at this interface by replacing less active saturated hydrocarbons with more reactive hydrophilic and hydrophobic species. Using oxygen to create greater chemical functionality improves the wettability of the surface. Figure 1 illustrates this effect of plasma on increasing the surface energy of a typical polypropylene plastic.

    Open-air plasma (plasma that can be used on a benchtop with no special environment) produces a stream of electrons, radicals and ions that strike the plastic surface with sufficient energy to cleave molecular bonds of most plastic substrates. This cleavage produces free radicals that react quickly in the presence of oxygen to form more chemically active groups such as hydroperoxide (HOO-), hydroxyl (HO-), carbonyl (C=O), and carboxyl (HOOC), groups. Even a relatively small number of these functional groups can be highly effective at improving adhesion to the plastic surface.

    Plasma Treatment and UV Coating Adhesion

    Atmospheric plasma treatment has been proven to be especially effective at improving adhesion of UV cure liquid coatings. Successes include using plasma to improve adhesion to polyamide fascia used in automotive interiors (Melamies, 2012). shows the beneficial effects of plasma treatment for coating biomedical devices (Oehr, 2003) and surface treatment for coating PC and PMMA plastics (Gururaj et al. 2011). 

    Contact angle measurements provide a highly accurate, and quantitative means to assess surface energy since a smaller contact angle is directly associated with greater wettability. Figure 2 shows the effect of plasm treatment on PC and PMMA plastics. Plasma increased the contact angle on the PC substrate from 80o before treatment, to 43o after plasma treatment and on PMMA from 65o before treatment to 55o after plasma treatment.

    The successful use of plasma for UV liquid coatings can also be extended to UV cure powder coatings.  UV powder was commercialized in 1998, and has expanded the applications for powder coating beyond metal goods to markets that require more heat-sensitive substrates such as plastics and wood.  The allure of UV powder coatings is that they combine the durability, cost efficiency, and environmentally friendly characteristics of conventional powder coatings with the low temperatures and fast speed afforded by UV crosslinking (Mills, 1998).  However, difficulties in achieving adhesion of UV powder coatings has also been reported (Skinner, 2003).

    Recently, some of these adhesion problems have been overcome using atmospheric plasma surface treatment. Plasma treatment is a safe, inexpensive and environmentally desirable alternative to traditional cleaning methods such as solvent wipe, reformulation or flame treatment. Active species in the oxygen combine with UV energy to drive a chemical reaction that removes surface contaminants, eliminating the need to clean the plastic surface manually. Plasma treatment is an effective process for both cleaning and activating difficult plastic surfaces prior to powder coating. 

    This article illustrates this solution with examples of standard test plaques molded from of various blends of polypropylene, ABS, polycarbonate, ABS/Polycarbonate, and Nylon. Plasma surface treatment was performed identically on each test panel at a line speed of 20 FPM using a Plasmatreat RD1004 rotating nozzle laboratory system.

    In order to promote electrostatic attraction of the powder coating to the non-conductive plastics, a thin (10-12 micron) conductive coating (Chemical Technology Inc. CTI-4386 or CTI-1693 or similar product) was spray applied and air dried. Next, an acrylated polyester UV curable powder coating was electrostatically applied at a film thickness of 55-60 microns. 

    The test panels were heated in a 230F electric convection oven for 10 minutes to allow the powder coating to melt and flow smoothly over the surface of the panel surface. The test plaques were cured using a (Fusion, 300W/in) gallium additive UV lamp.

    Full cure was confirmed by using 50 double rubs of methyl ethyl ketone, with no measurable loss using a 60o gloss meter.  Adhesion on each panel was evaluated using standard crosshatch adhesion test method ASTM D 3359 (see Table 2).

    This work provides several interesting insights.  First, plasma treatment had a pronounced improvement on coating adhesion for a number of substrates. Polypropylene, polycarbonate, ABS and ABS/PC panels which had no coating adhesion without surface treatment, showed excellent adhesion after atmospheric plasma treatment (see Figure 3). Second, there is still work to be done. For example, the polypropylene tested according to this method did not produce the same level of adhesion as we obtained on ABS or ABS/polycarbonate blends and we could not obtain adequate adhesion to Nylon 6 with plasma surface treatment conditions test so far. Further improvements may be achievable with refinement of the surface treatment process. 

    Another important observation is that while Some coating and substrate combinations (for example the ABS/polycarbonate blend used here) sufficiently might work well without surface treatment, this does not mean that plasma provides no added benefit. Since many manufacturers report turning to using regrind or recycled materials to reduce cost, plasma provides added insurance against failures by controlling the process even when the resin composition might change from batch to batch.

    We should also point out that our testing intentionally used a “stock” UV powder coating and standard plasma lab system. Since it is common practice to tweak the powder chemistry or fine-tune the plasma settings to optimize adhesion, we consider these results even more illuminating. The fact that the majority of powder/substrate combinations showed robust evidence that good results are possible without much fuss.  In three of the four cases plasma treatment made the difference between an acceptable and unacceptable process. 

    Certainly follow up work can focus on testing with variants of the powder coating, and different surface treatment parameters to improve the adhesion of UV powder coating both to these substrates, and to other popular plastics such as SMC, BMC,  and Nylon.

    This article shows how atmospheric plasma treatment can overcome adhesion failures commonly associated with UV liquid and powder coatings to plastic. Our testing also suggests that plasma surface treatment may offer a robust solution to applying a wide selection UV powder to a number of common plastics. 

    Our initial results provide evidence that plasma treatment yields acceptable results on otherwise un-coatable surfaces. Plasma offers a safe, cost-efficient, and environmentally friendly means for improving the performance of both liquid and powder UV coatings for a growing range of plastic applications. 

    This paper was originally presented at the 2nd Biennial Eastern Coatings Show, June 1-4 in Atlantic City, New Jersey.

    Acknowledgements

    The authors wish to thank Kevin Biller, and the research staff at the Powder Coating Research Group, Columbus, Ohio for their expertise, help and dedication to this project. 

    References

    1.   Burak, L.,(2003). Ensuring Proper Adhesion of UV- Curable Coatings to Plastic Substrates, Paint & Coatings Industry, March 2003
    2.   Cohen, G., (2012), UV/EB Market Trends, RadTech Report. 14:2 pp. 44-48
    3.   Gururaj,T., Subasri, R., Raju,K.R.C., Padmanabham, G. (2011). Effect of plasma pretreatment on adhesion and mechanical properties of UV-curable coatings on plastics. Applied Surface Science, 257(9), 4360-4364.
    4.   Jian, Y., He, Y., Jiang, T., Li, C., Yang, W., & Nie, J. (2013). Volume shrinkage of UV-curable coating formulation investigated by real-time laser reflection method. Journal of Coatings Technology and Research, 1-7.
    5.   Kaute, D., (2003). Plasma Technology Transforms Traditional Pain Line into High Speed Compact Line, Radtech Report, November/December 2003, pp. 33-35
    6.   Knoblauch, M., Schwarb, R., (2012), Innovation and Sustainability Drive UV-Cured Powder Coating Development, Plastics Decorating, July/August 2012, pp. 14-17 
    7.   Little, M., Plastic Man, Products Finishing, January 2005
    8.   Loof, R., (2001). UV/EB Gains Regulatory Recognition, Radtech Report, May/June 2001,  pp. 18-19
    9.   Meichsner, J., Zeuner, M., Kramers, B., Nitschke, M., Rochotzki, R., Barucki, K., (1998) Surf. Coat. Technol. 98, 1565.
    10. Melamies, I., (2012), Power Treatment: Plasma for the Perfect Design, Paint & Coatings Industry, June 2012, pp. 42-43
    11. Mills, P. (1998), UV Powder, the Marriage of Two Comlaint Technologies, Metal Finishing, January 1998, pp. 38-41
    12. Oehr, C. (2003). Plasma surface modification of polymers for biomedical use. Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms, 208, 40-47.
    13. Ryntz, R.A.,(1998). Adhesion to Plastics: Molding and Paintability, Gobal Press
    14. Ryntz, R.A., (1994). Coating adhesion to low surface free energy substrates, Progress in Organic Coatings, 25, pp. 73-83
    15. Schwalm, R. (2006). UV coatings: basics, recent developments and new applications. Elsevier.
    16. Schwarb, R., Knoblauch, M., (2011). New Opportunities for UV-Curable Powder Coatings UV-curable powder coatings continue to grow in demand. Coatings World, November, 2011.
    17. Skinner, D., (2003). UV Curing in the Plastics Component Industry, Radtech Report, July/August 2003, pp. 19-23
    18. Walton, A., (20-12). Sustainable, Safe and High Quality UV-Cure Powder Coating for Wood Substrates, Presented at the 5th Wood Coatings Conference, University of North Carolina, Greensboro, NC, September 20-21, 2012)
    19. Whitfield, J.K., (1995). Overview of Powder Coating Technology and EPA’s Powder Coating Research, Presented at the Low- / No- VOC Coating Technologies 2nd Biennial International Conference, Durham, NC, March, 1995
    Related Searches
    • waterborne
    • olin
    • polymers
    • conference
    Related Knowledge Center
    • Additives
    • Wood Coatings
    • Radcure Coatings
    Suggested For You
    PPG Introduces Premium Iso-free Primer Surfacer, Catalyst PPG Introduces Premium Iso-free Primer Surfacer, Catalyst
    Raw Material Suppliers, Distributors Part of Recent M&A Activity Raw Material Suppliers, Distributors Part of Recent M&A Activity
    IFS Coatings Launches IFS Pureflex FBE for Rebar IFS Coatings Launches IFS Pureflex FBE for Rebar
    AkzoNobel Opens R&D Lab Dedicated to Low Cure Powder Coatings AkzoNobel Opens R&D Lab Dedicated to Low Cure Powder Coatings
    AkzoNobel Offers 100% UV Cured Wood Coatings AkzoNobel Offers 100% UV Cured Wood Coatings
    IFS Coatings Launches IFS Puroplaz PE20 Texture IFS Coatings Launches IFS Puroplaz PE20 Texture
    Keyland Polymer UV Powder, LLC Launches UVMax Defender Keyland Polymer UV Powder, LLC Launches UVMax Defender
    LINE-X Launches Dealer Program with International Truck LINE-X Launches Dealer Program with International Truck
    Senior Laboratory Researcher Senior Laboratory Researcher
    Axalta Launches 2 Imron Elite products Axalta Launches 2 Imron Elite products
    AkzoNobel Supplying Powder Coatings for Landmark Water Pipeline in China AkzoNobel Supplying Powder Coatings for Landmark Water Pipeline in China
    IFS Coatings Announce Carbon Offset Program IFS Coatings Announce Carbon Offset Program
    Axalta Powder Coatings Presents SuprAnodic Collection Axalta Powder Coatings Presents SuprAnodic Collection
    HMG Paints Earns HMG Paints Earns 'Made in Britain' Accreditation
    Waterborne 2021 Registration Open Waterborne 2021 Registration Open

    Related Features

    • Additives

      Additives Directory

      Here is a look at the latest offerings from select additives suppliers. For more information on the products listed, please contact the company directly.
      03.13.20

    • Industrial Coatings | Powder Coatings
      High Performance Pigments Market

      High Performance Pigments Market

      With an overall value of $4.76 billion, the market for high performance pigments is poised for steady growth worldwide.
      Kerry Pianoforte, Editor 08.10.16

    • Architectural Coatings | Industrial Coatings | Marine Coatings | Wood Coatings
      Asia Pacific Report

      Asia Pacific Report

      Key findings indicate that the market for paint and coatings in the Asia Pacific region is poised for more growth.
      08.10.16


    • Architectural Coatings | Wood Coatings
      Coatings World and Ringier Events Host 14th Annual China Coatings Summit

      Coatings World and Ringier Events Host 14th Annual China Coatings Summit

      This annual event jointly organized by Coatings World and Ringier was held May 24-25 in Shanghai.
      Kerry Pianoforte, Editor 07.15.16

    • Additives | Architectural Coatings | Pigments | Solvents
      Is There A Correlation Between Contact Angle And Stain Repellency?

      Is There A Correlation Between Contact Angle And Stain Repellency?

      ...
      Daniel J. Mania 07.14.16

    • Additives | Adhesives and Sealants | Wood Coatings

      Resins Supplier Directory

      Here is a look at the latest offerings from select resins suppliers. For more information on the products listed, please cont
      07.14.16


    • Additives | Binders

      Unique Solutions to Regulatory Concerns Affecting Cobalt and MEKO

      ...
      Richard Najdusak and Dr. Franjo Gol 06.08.16

    • Automotive Coatings | Industrial Coatings | Pigments | Powder Coatings | Price Increases
      Metallic Pigments

      Metallic Pigments

      Diversified trends in automotive colors and increased consumer competition are driving this market forward.
      Catherine Diamond, Associate Editor 06.08.16

    • Architectural Coatings | Automotive Coatings | Automotive Refinish | Industrial Coatings | Powder Coatings
      Latin America Paint And Coatings Update 2016

      Latin America Paint And Coatings Update 2016

      Regional demand is likely to exceed GDP in the region.
      Charles W. Thurston, Latin America Correspondent 06.08.16


    • Industrial Coatings | Powder Coatings
      The Industrial Coatings Market

      The Industrial Coatings Market

      The market for industrial and protective coatings has potential for growth in a number of key markets.
      Kerry Pianoforte, Editor 06.08.16

    • Additives | Adhesives and Sealants | Architectural Coatings | Powder Coatings | Solvents
      Resins Update

      Resins Update

      All segments of this market are expected to grow steadily, particularly in Asia-Pacific.
      Catherine Diamond, Associate Editor 04.08.16

    • Additives | Architectural Coatings
      Low- and Zero-VOC Coatings

      Low- and Zero-VOC Coatings

      Low- and zero-VOC coatings are moving out of the specialty category and are becoming a must-have option.
      Kerry Pianoforte, Editor 04.08.16


    • Additives | Radcure Coatings | Wood Coatings

      Radiation-Curing Technologies

      ...
      Kerry Pianoforte, Editor 04.08.16

    • Wood Coatings

      RADTECH 2016 to Focus on End Uses, New Technologies

      Leaders from P&G, Ford Motor, Toyota, PepsiCo and Nestlé will provide insights on using energy curable technologies.
      David Savastano, Ink World Editor 04.08.16

    • Wood Coatings
      LED Curing Technology for Coatings

      LED Curing Technology for Coatings

      ...
      Stacy Hoge, Marketing Communications Manager, Phoseon Technology 04.08.16

    Trending
    • Raw Material Price Increases Pile Pressure On Paint Manufacturers
    • Hempel Announces Global Price Increase
    • Hempel Acquiring Wattyl Australia, New Zealand
    • ChemQuest Hires Rich Gibson
    • Tennant Company Completes Sale Of Coatings Business To Sherwin-Williams
    Breaking News
    • Nippon Paint Marine Wins Korea Export Award
    • ECOS Paints Launches Lisa Tharp Colors
    • PPG Introduces Premium Iso-free Primer Surfacer, Catalyst
    • Universal Display Corporation, PPG Expand Global Production of UniversalPHOLED Materials
    • OQ Chemicals Increases Carboxylic Acids, Esters Prices
    View Breaking News >
    CURRENT ISSUE

    February 2021

    • Mixing Equipment Directory
    • The Wood Coatings Market
    • Antimicrobial Coatings Market
    • View More >

    Cookies help us to provide you with an excellent service. By using our website, you declare yourself in agreement with our use of cookies.
    You can obtain detailed information about the use of cookies on our website by clicking on "More information”.

    • About Us
    • Privacy Policy
    • Terms And Conditions
    • Contact Us

    follow us

    Subscribe
    Nutraceuticals World

    Latest Breaking News From Nutraceuticals World

    Preliminary Study Links Markers of Impaired Bone Health to Vegan Diet
    Refined Grains Linked to Heart Attack Risk, Early Death
    Kappa Bioscience Extends Research Partnership For COVID-19 Research
    Coatings World

    Latest Breaking News From Coatings World

    Nippon Paint Marine Wins Korea Export Award
    Universal Display Corporation, PPG Expand Global Production of UniversalPHOLED Materials
    PPG Introduces Premium Iso-free Primer Surfacer, Catalyst
    Medical Product Outsourcing

    Latest Breaking News From Medical Product Outsourcing

    January AI Raises $8.8 Million in New Funding
    FDA Clears Ava Fertility Tracking Wearable Device
    First Patient in Europe Treated With Diamondback 360 Coronary Orbital Atherectomy System
    Contract Pharma

    Latest Breaking News From Contract Pharma

    Spark Therapeutics Appoints CTO
    Cryoport Launches ESG Program
    U.S. Govt. Purchases 100k Doses of Lilly's COVID-19 Antibody Cocktail
    Beauty Packaging

    Latest Breaking News From Beauty Packaging

    The Top Beauty Products of 2021, According to HelloGiggles
    Estée Lauder Taps Ana de Armas as Global Brand Ambassador
    Sephora Announces Significant Expansion
    Happi

    Latest Breaking News From Happi

    Cosmetic Chemical Sales To Post CAGR 5.8% To 2025
    ACI Urges Senate to Approve Regan as EPA Administrator
    Estée Lauder Signs Actress Ana de Armas
    Ink World

    Latest Breaking News From Ink World

    Etiflex Enters New Markets with Nilpeter FA-22 Installation
    Hydrocarbon Solvents Market to Surpass $8.1 Billion by 2030
    Marshall & Bruce Adds Koenig & Bauer Rapida 106 41-Inch Seven-Color Press
    Label & Narrow Web

    Latest Breaking News From Label & Narrow Web

    FTA converts Forum & INFOFLEX to virtual events
    Xeikon launches two new digital label printing presses
    UFlex adds capacity in packaging films
    Nonwovens Industry

    Latest Breaking News From Nonwovens Industry

    Texas Medical Technology Partners with My Protect Kit
    Mexico City Single-Use Plastics Ban Leads to Tampon Shortage
    Believe Diapers Launch in U.S.
    Orthopedic Design & Technology

    Latest Breaking News From Orthopedic Design & Technology

    Fusion Robotics Receives FDA Clearance for Spinal Navigation and Robotics System
    Kaia Health Unveils Next-Gen Complete MSK Care Solutions
    First Implantation of CTL Amedica's Minimally Invasive Flex Tower
    Printed Electronics Now

    Latest Breaking News From Printed Electronics Now

    Comercial Kywi Improves Customer Service, Front-Store Operations with Zebra Mobile Solution
    Global Printed Circuit Board Market Projected to Reach $69.32 Billion by 2027
    Global Smart Glass Market to Register 6.8% CAGR Between 2021-28: Grand View Research

    Copyright © 2021 Rodman Media. All rights reserved. Use of this constitutes acceptance of our privacy policy The material on this site may not be reproduced, distributed, transmitted, or otherwise used, except with the prior written permission of Rodman Media.

    AD BLOCKER DETECTED

    Our website is made possible by displaying online advertisements to our visitors.
    Please consider supporting us by disabling your ad blocker.


    FREE SUBSCRIPTION Already a subscriber? Login